1102 Gel Coat Resin isophthalic acid type

short description:

1102 gel coat resin is isophthalic acid, cis-tincture, neopentyl glycol and other standard diols as the main raw materials of m-benzene-neopentyl glycol type unsaturated polyester gel coat resin, which has been dissolved in styrene The cross-linking monomer contains thixotropic additives, with medium viscosity and medium reactivity.


Product Detail

Product Tags


PROPERTY

• 1102 Gel coat resin has excellent weather resistance, good strength, hardness and toughness, small shrinkage, and good product transparency.

APPLICATION

•It is suitable for the production of brush coating process, the surface decoration layer and protective layer of FRP products or sanitary ware products,ect
QUALITY INDEX

 

ITEM

 

Range

 

Unit

 

Test Method

Appearance

White paste viscous liquid    
Acidity

13-20

mgKOH/g

GB/T 2895-2008

Viscosity, cps 25℃

0.8-1. 2

Pa. s

GB/T 7193-2008

Gel time, min 25℃

8-18

min

GB/T 7193-2008

Solid content, %

55-71

%

GB/T 7193-2008

Thermal stability,

 80℃

24

h

GB/T 7193-2008

Thixotropic index, 25°C

4. 0-6. 0

Tips: Gel time test: 25°G water bath, add 0.9g T-8M (Newsolar,l%Co) and o.9g MOiAta-ljobei) to 50g resin.

MECHANICAL PROPERTY OF CASTING

 

ITEM

 

Range

 

Unit

 

Test Method

Barcol hardness

42

GB/T 3854-2005

Heat Distortion temperature

62

°C

GB/T 1634-2004

Elongation at break

2.5

%

GB/T 2567-2008

Tensile strength

60

MPa

GB/T 2567-2008

Tensile modulus

3100

MPa

GB/T 2567-2008

Flexural Strength

115

MPa

GB/T 2567-2008

Flexural modulus

3200

MPa

GB/T 2567-2008

MEMO: Performance standard of resin casting body: Q/320411 BES002-2014

PACKING AND STORAGE

• Packing of gel coat resin: 20 kg net, metal drum

NOTE

• All information in this catalog is based on GB/T8237-2005 standard tests, only for reference; maybe differ from the actual test data.
• In the production process of using resin products, because the performance of user products is affected by multiple factors, it is necessary for users to test themselves before selecting and using resin products.
• Unsaturated polyester resins are unstable and should be stored below 25°C in a cool shade, conveyance in refrigeration car or in nighttime, averting from sunshine.
•Any unsuitable condition of storage and conveyance will cause the shortening of shelf life.

INSTRUCTION

• 1102 gel coat resin does not contain wax and accelerator, and contains thixotropic additives.
• The mold should be processed in a standardized manner before preparation to meet the requirements of gel coat construction.
• Color paste recommendation: special active color paste for gel coat, 3-5%. The compatibility and hiding power of the color paste should be confirmed by field test.
• Recommended curing system: special curing agent for gel coat MEKP, 1.A2.5%; special accelerator for gel coat, 0.5~2%, confirmed by field test during application.
• Recommended dosage of gel coat: wet film thickness 0. 4-0. 6tmn, dosage 500~700g/m2, gel coat is too thin and easy to wrinkle or expose, too thick and easy to sag
crack or blisters, uneven thickness and easy to rise Wrinkles or partial discoloration, etc.
• When the gel coat gel is not sticky to your hands, the next process (upper reinforcement layer) is made. Too early or too late, it is easy to cause wrinkles, fiber exposure, local discoloration or delamination, mold release, cracks, cracks and other problems.
• It is recommended to choose 2202 gel coat resin for spraying process.

 